Description
1. High impact polystyrene/ HIPS
2. HIPS 7240 is high impact resistance for extrusion molding
3. Application: The product is used for making packaging, sheet
Note: These are typical properties, only and are not to be construed as specifications. Users should confirm
Results by their own tests.
|
Physical property |
Rating |
Test method |
|
Density |
1.04g/cm3 |
ISO 1183 |
|
MFR(200 ºC/5.0kg) |
4.5 g/10min |
ISO 1133 |
|
Mechanical property |
Rating |
Test method |
|
Tensile stress at yield |
23.0 MPa |
ISO 527-2 |
|
Tensile stress at break |
21.0 MPa |
ISO 527-2 |
|
Tensile modulus |
1950 MPa |
ISO 527-2 |
|
Flexural Strength |
1850 MPa |
ISO 178 |
|
Impact property |
Rating |
Test method |
|
Notch impact strength(23 ºC) |
11.0kJ/M2 |
ISO 180/lA |
|
Thermal property |
Rating |
Test method |
|
Vicat softening point |
97.0 ºC |
ISO 306/A50 |
|
Vicat softening point |
87.0 ºC |
ISO 306/B50 |
|
Heat deflection temperature(1.8MPa, unannealed) |
74.0 ºC |
ISO 75-2/A |
|
Heat deflection temperature(1.8MPa, annealing) |
90.0 ºC |
ISO 75-2/A |
|
Heat deflection temperature(1.8MPa) |
89.5 ºC |
ISO 75-22 |
We guaranteed products at a competitive price and high quality. At present, our products have a very good sale in domestic and overseas market. We wish to cooperate with you to create a bright future and mutual benefit. Much appreciation for your prompt attention in advance, we are eager to look forward to hearing from you soon.