EPS Beads Granules Expandable Polystyrene Resin Fire Flame Retardant Regular Common Grade King Pearl Brand

E.P.S. (Expandable Poly Styrene) is a lightweight, rigid, plastic foam insulation material produced from solid particles of polystyrene. Expansion is achieved by virtue of small amounts of pentane gas dissolved into the polystyrene base material during production. The gas expands under the action of heat, applied as steam, to form perfectly closed cells of EPS. These cells occupy approximately 40 times the volume of the original polystyrene bead. The EPS beads are then molded into appropriate forms suited to their application. Products made from foamed polystyrene are nearly ubiquitous, for example packing materials, insulation, and foam drink cups.
 
EPS Characteristics:  
Good flame-retardant, good frothing good preserving, good binding and low heat-conducting rate.Oxygen index over 30 (testing after 7-14 days flowing)          
         
EPS Application:    
This Flame retardant grade EPS can be used as building-materials, materials for heat preservation, thermal insulation and for packing precision instruments    
 
EPS Specifications:

Flame Retardant Grade	Specification	Bead Size(diameter)	Expandable Rate (one time)	Foam Density
		mm	times	g/l
	QJ-202	1.60-2.50	70-85	3-5
	QJ-301	1.20-1.65	60-70	5-8
	QJ-302	1.00-1.25	50-65	7-11
	QJ-303	0.75-1.00	50-60	9-15
	QJ-401	0.65-0.80	45-55	14-18
	QJ-501	0.45-0.85	35-50	18-above
	QJ-601	0.40-0.50	30-40	18-above
	QJ-701	0.25-0.40	30-40	18-above

  
Packaging: 25kg/paper bag, 17Tons/20ft Container
Storage: The EPS series products of our company need to be put on the place where it is cool and ventilated, keep the storage temperature below 20°C in order to minimize the lost of frothing agents from escaping. The lower the temperature is, the better the quality is. The products should avoid rain, fog, snow and lighting up from the sun, static electricity and flame. Once the package material of the products is open, it should be used up as quickly as possible. Otherwise, the remaining EPS might lose its function due to escaping of foaming agents. If the EPS is stored too long, the expandable times might decrease.