GREEN LEAF Handbook of industrial protective coatings |
Vinyl ester glass flake coating PE902 |
|||||
Application |
* Solvent-free paint, room temperature curing, construction one time can get thick, dry inside and outside, which has excellent corrosion resistance.Is the best overall performance of glass flake coating, chemical resistance is superior to epoxy and unsaturated polyester glass flake coating. * Added glass flake, alternating and covered with each other in the film, the water, salt, oxygen, acid and other corrosive chemicals penetrate immersion uneasily , and get good protection. * For heavy anti-corrosion coating of chemical equipment , such as the top lining of an empty tower in sulfuric acid production plants (the medium is 80 degree centigrade, 15% sulfuric acid, a small amount of hydrochloric acid and HF and SO2, SO3), pipe lining, large-scale brine Subsidence of chlor-alkali production devices and the flue gas desulfurization tower of ethylene plant and so on.To replace the ceramic, rubber and glass reinforced plastic lining, significant economic benefits. |
|||||
Products Introduction | Three components, pre-construction mixed, Part A is alkene ester resin, glass flake, and the composition of the paint additives, B and C were, respectively, as initiator and promoter. | |||||
Product data | Solid volume | >98% | ||||
Dry film thickness | 0.5-1 mm each | |||||
Theoretical spreading rate | 0.93-1.86m2/kg | |||||
Practical Coverage | In connection with loss coefficient and dry film thickness | |||||
Works described in detail | Mixing ratio | A: B: C = 100:1.5:1 (weight ratio) | ||||
Scratch coat | Recommended | |||||
Brush or roller | Can be use | |||||
Airless spray | Recommended use: The total output fluid pressure adjust to the consteuction temperature and viscosity of liquid | |||||
Conventional spray | Not applicable | |||||
Thinner | No | |||||
Paint equipment cleaning agent | BW115 | |||||
Use of |
25degree centigrade-40min 35degree centigrade-15min |
|||||
Shelf | 6months | |||||
Curing time (induction period) | No, after mixing the three components can be used immediately. | |||||
Drying time | ||||||
Substrate temperature | Surface dry (h) | Completely dry (h) | Repeat brushing interval | |||
The shortest | The longest | |||||
25 degree centigrade 35 degree centigrade |
24 12 |
24 12 |
24h 12h |
7days 7days |
||
Storage and management | Storage | Store in a cool, dry place,resistant to water and fire, environmental temperature does not exceed 45 degree centigrade | ||||
Packing |
A:20KG in 20L containers B: 300g in a vial C: 200g in a vial |
|||||
Proportion | 1.05kg/ liter | |||||
Technical requirements and surface treatment |
The not coated primer surface blasting or sandblasting of Sa2.5 level.Surface roughness of 50-100 microns | |||||
Restrictions |
* Before use , well mixed A and C, then add Part B, stir evenly, then use. Avoid mixing B and C directly. *Using this product, the existing service should be active, mixed evenly and thoroughly,use up in the guarantee period in order to avoid gel waste. *The range of application of this paint and detailed construction instructions, please consult us. |
|||||