Virgin/Recycled Polyethylene Plastic Material /PE100 /PE80 /HDPE/LDPE/LLDPE

Product Specifications

Prod Model:	PE100 /PE80
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Packaging Details:	25kgs/Bag 16-18mt/20'f 26-28mt/40'f
Usage:	General Plastics
Color:	White

Product Description

 polyethylene/PE100
Composed of ethylene polymerization of polymers
Polyethylene in accordance with the polymerization methods, different high and low molecular weight, chain structure,
high density polyethylene, low density polyethylene and linear low density polyethylene.
HDPE PE 80
Density(g/cm3)              0.95
Power Ash%                 0.01
Tensile Strength (MPa)      22
Elongation At Break%         600
Izod Impact Strength (J/M)--
Environmental stress-cracking  1500
Impact Embitterment temperature°C --

HDPE PE 100
Melt Flow Rate(g/10min)       0.04
Density(g/cm3)              0.949
Power Ash%                 0.01
Tensile Strength (MPa)      22
Elongation At Break%          600
Izod Impact Strength (J/M) --
Environmental stress-cracking  10000
Impact Embrittlement temperature°C --
HDPE manufacturer!Free sample!Virgin/Recycled HDPE granules,PE80,PE100
Specification:
Film Grade

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

 
Blow Molding Grade

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

 
Injection Grade

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

Application:
HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.
HDPE is suitable for many plastic molding methods. Blow molding can be used for making various types of bottles, cans and industrial tanks and barrels. Injection molding is used for making various containers and goods of daily use, such as basins, barrels and baskets and furniture. Extrusion molding is used for making pipes, strapping tapes, fibers and single filaments and can also be used for making wires & cables covering materials and synthetic paper. After a large amount of inorganic filler is added, HDPE can also be used as an alternative to timber and cardboards for making calcium plastic packing containers, furniture, doors and windows.