Nominal Inner Diameter | Wall Thickness Min. | Tolerance | ||
Inner Dia. | Wall Thickness less than 10mm | Wall Thickness more than 10mm | ||
8-30 (multiples of 2 or 5) | 1.5 | ±0.4 | ± 0.5 | ± 1.0 |
32-80 (multiples of 2 or 5) | 1.5 | ±0.5 | ||
85-150 (multiples of 5) | 2.0 | ±0.5 | ||
155-350 (multiples of 5) | 2.0 | ±0.7 | ||
355-500 (multiples of 5) | 2.0 | ±1.0 |
PROPERTIES | UNIT | STANDARD VALUE |
Flexural strength A: Under normal conditions | MPa | ≥300 |
Compressive strength | MPa | ≥175 |
Bonding strength | MPa | ≥200 |
Breakdown voltage parallel to laminations (in transformer oil 90±2°C) | kV | ≥40 |
Dielectric strength perpendicular to laminations (withstand voltage) (in oil 90±2°C) 2.0mm in thickness | MV/m | ≥9.0 |
Insulation resistance Impregnated in water, D-24/23 | MΩ | ≥1000 |
Density | g/cm3 | 1.70-1.90 |
Water absorption D-24/23 | mg/cm2 | ≤1.5 |
Flammability | class | FV0 |
Prod Model: | 3841 |
---|---|
Markets: | North America,South America,Southeast Asia,Africa,Mid East |
Length: | 1000mm-1100mm |
Nominal Diameter: | 6mm-200mm |
Diameter: | 6-50mm |
Density: | >1.70g/cm3 |
Flexural Strength: | >241.3MPa |
Compressive Strength: | >241.3 MPa |
Breakdown Voltage Parallel To Layers,at: | >15 Kv |
Application: | Switch Baseplate |
Chemistry: | Inorganic Insulation |
Material: | Fiberglass |
Thermal Rating: | B 130 |
Maximum Voltage: | 20KV~100KV |
Type: | Insulation Rod |
Color: | Green,Blue ,Black Color |
Brand: | Chr |