| Coating Property: |
Chemical type Polyester-Epoxy Resin Particle size Suitable for electrostatic spraying Density 1.2-1.8g/cm3(depend on color) Storage condition Dry and cool place Period of validity 6months( under 30C) Product code EP Series Temperature of baking 200C 10Min 190C 15Min 180C 17Min Semimatt powder coatings need to add 5min |
| Test Condition: |
All chemical and physical properties are laboratory test results under certain conditions (except particular statement), it is reference only for coating application. Actual performance is still based on the product end-use environment Substrate 0.5 mm cold rolled steel (bending using tinplate) Pre-treatment zinc phosphating (Bonderite 1000) Recommended film thickness 50-70 microns (tested film thickness 60um)Temperature of baking 200C 10min(temperature of workpiece) 180C 17min(temperature of workpiece) |
| Physical Properties: |
Flexibility GB/T 6742 3mm pass Adhesion GB/T 9286-1998 0~1grade Cupping test GB/T 9753 6mm pass Hardness GB/T6739 1H Impact resistance GB/T 1732-1993 50 cm*kg |
| Chemical Properties: |
Salt spray GB/T 1771 Pass- corrosion within 2mm (250 hours) Moisture resistance GB/T 1740 Pass- no blistering and without losing the gloss(1000 hours) Soaked in distilled water BS3900-F7 Pass-no blistering and without losing the gloss(240 hours) Chemical resistance Excellent(testing at room temperature use general acid and oil) Outdoor persistence Exposure outdoor will change the color, after 6-12months exposure outdoor, there will be minor chalking |
| Pre-treatment: | All metal substrate is required to be degreasing, ferrous metals use zinc or iron phosphating, aluminum recommend chromium treatment to improve the corrosion resistance. Generally substrate need to meet the neutral phosphide 48 hours, phosphate coating no abnormal. |
| Application: |
EP Series Powder Coatings can be manual or automatic electrostatic spray gun coating, the powder coating can be recycled by a appropriate recovery system, recycled powder with new powder ratio is roughly 3:7, the specific ratio is according to the actual situation. The powder coating thickness is usually controlled less than 100 microns, in order to avoid the stream hung and pinhole. |
| Other Information: |
EP Series Powder Coating can have texture of aluminum silver and copper gold surface effect, but it has problems with the scratches, oxidation and resistant to fingerprints, it need to cover a layer of transparent powder to overcome these drawbacks. Transparent powder should be sprayed within two hours after spraying metal powder. Handling gloves need to keep clean. LEP (quick response) is applied to the field of low temperature or short curing time: Product Code: L series Curing Temperature: 160C*15 minutes (workpiece temperature) /180C*8 minutes (workpiece temperature) EP Series of low-light powder in the case of flexibility, performance declined, anti-yellowing properties deteriorate. EP Series of sand grain powder which gloss less than 10%, its aging properties, corrosion resistance, and flexible performance will decline more. EP Series wrinkle powder because of its characteristics, is poor resistance of salt spray, please be carefully chosen according to the application requirements. |
| Security Reminder: | Do not eat, drink and smell while using. Do not breathe dust. Please wear the necessary labor protection supplies. Maintain spray equipment is well grounded. |
| Statement: |
The information provided in this manual is not unlimited. Users have to bear the risk for the products before our professionals confirmed in writing to meet the needs of product’s use. We strive to ensure that our product recommendations is correct. (whether or not included in this manual), But we can not control over the substrate, pre-treatment and other factors that affect the use and application. Unless we have confirmed in writing to meet the requirements, we will not accept the responsibility of any loss and damage caused by the use and application of products. The information in this manual depicts obligation to continue to be updated with the experience and our ongoing product development. |
| Prod Model: | EP28033R |
|---|---|
| Markets: | North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe |
| Chemical Type: | Epoxy-Polyester |
| Use: | Furniture Paint |
| Method: | Spray |
| Level: | Finish Coat |
| Substrate: | Steel |
| Appearance: | High Solid |
| Main Raw Material: | Epoxy-Polyester |
| Certification: | SGS RoHS ISO9001 |