SE2617 is epoxy adhesive with very high tensile and high curing speed
Features
1. Resistance of moisture, pollution and other atmospheric constituent
2. High tensile, excellent adhesive property
3. Excellent pollution resistance, the demand of preprocess is low
4. Solvent free, no by-product in curing
5. Stable mechanical and electricity in -45º C~120º C
6. Excellent adhesive performance with fiberglass and metal sheet
Use
Epoxy Adhesive for metal, glass, plastic, paper, rubber, fabric, etc.
Operation
1. Mix Part A and Part B by 1: 1 evenly, seal the parts after using.
2. Stirring by one direction for avoiding the bubbles; The frame and bottom also need to be stirred evenly, or it will cause not cure situation.
3. Low temperature will slow the curing speed, if the primary strength can't get, the application environment needs to do constant temperature control.
4. Taking care of the material mouth seal in using
Package
Cartridge: 2*25ml
Barrel: 2*1KG
Shelf life: 12 months
Safety Operation Material
MSDS isn't included here. Please read TDS, MSDS and label carefully before operation. You can get MSDS from Sepuna or other distributors, or mail to service center sepuna046@sepuna. Cn, or call +86-415924279222
Product Warranty
All product properties and application details based on information believe to be reliable and accurate. But you still need to test its property and safety before application. The advices we supply don't apply in any circumstances. Sepuna don't make assurance of any other applications outside the specification until Sepuna supply a special written guarantee. Sepuna is only responsible to replace or refund if this product is defective within the warranty period stated above. Sepuna makes it clear that will not be liable of any accidents.
Properties before curing |
Part |
2617A |
2617B |
Component |
polysiloxane |
Hydrogen polysiloxane |
Appearance |
Transparent thickliquid |
Pale yellow thickliquid |
Viscosity, mPa.s(25ºC) |
10000-12000 |
5000-8000 |
Density, g/cm3(25ºC) |
1.1 |
1.1 |
Mixture/mass ratio |
A:B = 100:100 |
Viscosity after mixing, mPa.s (25ºC) |
9000-11000 |
Operation time after mixing, min(25ºC) |
2min |
Preliminary curing time(min) |
5 |
Properties after curing |
Hardness, Shore D |
80 |
Shear strength, Mpa,Al/Al |
10 |
Shear strength, Mpa, Fe/ Fe |
12 |
Expansion parameterμm/(m,ºC) |
44 |
Water absorption 24h,25ºC,% |
<0.3 |
Dielectric strength, KV/mm |
>20 |
Loss factor(1 MHz) |
0.014 |
Dielectric constant (1 MHz) |
3.53 |
Volume resistance DC500V, Ω@cm |
1.2×1015 |
Founded in DEC. 2003, SEPUNA has been engaged in researching, manufacturing and marketing automobile sealant and adhesive for 9 years.
Since the foundation, SEPUNA Chemical has been focusing on adhesive's researching and application. Then in 2005, We acquired PUNADE technology which is from Switzerland.
Within 9 years, SEPUNA mainly develops Silicone, Polyurethane and Epoxy resin adhesives. And in the future, we will enlarge our line to Unsaturated, Natural and Acrylic Resin adhesive.
After 9 years' improvement, by the keep researching and innovation, SEPUNA is already a mature adhesive supplier with the core competitiveness.