20mm Wall Floor Thermal Building Material

Product Specifications

Prod Model:	1220*2440mm
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Density:	1.0-1.3G/Cm3
Surface Treatment:	Standard or Slurry Treatment
Backside Treatment:	Standard or Sanding
Fire Resistant Time:	3 Hours
Delievery:	15 Days
Certificate:	CE,ASTM ,SGS,ISO9001:2000 QC System
Sample:	Free
Quality:	Grade a
Grade:	Grade A
Thickness:	15mm
Appearance:	Panel
Material:	Non-asbestos
Type:	Magnesium Oxide Board
Surface Finishing:	Glossy
Shape:	Square
Refractory Temperature:	Over 2000 ℃
Usage:	Building
Color:	Red,Green,Grey,White and So on
Edge:	Square,Grooved,Tapered,Beveled

Product Description

20mm thick Fireproof flooring


OCM MGO flooring is manufactured by using special craft through totally automatic product line. The materials of magnesium fireproof board are Magnesia(MGO), Magnesium Chlorid(Mgcl2)and reinforced fiber glass mesh and so on.

Main characteristic:
OCM MGO flooring has features as follows:
(1). Non-flammability: OCM MGO flooring is non-flammable and conforms to the national grade A1 standard (GB8624-2006 Grade A1). In case of fire, the board will not burn and not give off poisonous smoke, and is ideal in multi storey building such as offices and apartments for escape routes and shaft wall, or dividing walls in commercial units.


(2)Water-proofing and moisture-proofing: The product is allowed to long-term expose to moist environment. Test results prove that after this material has been immersed in water for one month, it keeps its original shape without deformation or expansion and its dry-wet deforming ratio is 0%.

(3)Problem-free: OCM MGO flooring provides good insulation against bugs, fungus and corrosion. It can last for a long-time and will not corrode.

(4)High-Strength and Lightweight: Owing to the density is not high, OCM flooring is light weight, in this case, it can decrease weight of building greatly. At the same time, the material is high-strength and not easy to be damaged.

(5)Easiness to construct: OCM MGO flooring is easy to cut, saw nail, stick. OCM MGO flooring has a smooth finish one side that can be grooved and jointed ready for decoration including wallpapering, painting, texture coat and veneer, and a rougher side for tiling.

(6)Environment: OCM MGO flooring does not contain any organic solvents, formaldehyde, asbestos, oils or other toxic substitances that can have a negative impact on the environment and waterways. As such, saw dust from OCM MGO flooring can safely be disposed off in landfills. Off-cuts of OCM MGO flooring can be reground and reused back at the production factory.

Thickness for flooring: 12mm, 15mm, 16mm, 18mm, 20mm and 25mm
Max length is 3800mm and Max width is 1220mm. Other size can be cut as your requirements.
Edge treatment can be tapered and grooved.

Testing Item	Data	Basis
Apparent densitye	0.85-1.5t/m 3	JC688-2006
Moisture content	≤8%	JC688-2006
Percentage of dry shrinkage	≤0.3%	JC688-2006
Percentage of water swelling	≤0.6%	JC688-2006
Screw_withdrawal force	≥70N/mm	JC688-2006
Dehalogenation resistance	No water and no moisture created	JC688-2006
Content of chloride ion	≤10%	JC688-2006
Fireproof performance	A1 non-flammability	GB8624-2006
Fire resistant time	2h	A 90mm-thick partition with 6mm mgo board on both sides of studs
Fire resistant time	4h	A 99mm-thick partition with 12mm mgo board on both sides of studs
Sound insulation	42dB	9mm MgO board+75 stud+50 rockwool
Bending strength	16MPa	9mm
Impacting strength	5.5Kj/m 2	9mm
Environment	No radioaction, asbestos or formaldehyde free	GB656-2001
Water permeability	No moisture or water	CECS9597
Alkali Resistance		CECS9597
Thermal conductivity	0.109	Average temperature: 30±5 Kcal/m°chr

Testing Item	Data	Basis
Apparent densitye	0.85-1.5t/m 3	JC688-2006
Moisture content	≤8%	JC688-2006
Percentage of dry shrinkage	≤0.3%	JC688-2006
Percentage of water swelling	≤0.6%	JC688-2006
Screw_withdrawal force	≥70N/mm	JC688-2006
Dehalogenation resistance	No water and no moisture created	JC688-2006
Content of chloride ion	≤10%	JC688-2006
Fireproof performance	A1 non-flammability	GB8624-2006
Fire resistant time	2h	A 90mm-thick partition with 6mm mgo board on both sides of studs
Fire resistant time	4h	A 99mm-thick partition with 12mm mgo board on both sides of studs
Sound insulation	42dB	9mm MgO board+75 stud+50 rockwool
Bending strength	16MPa	9mm
Impacting strength	5.5Kj/m 2	9mm
Environment	No radioaction, asbestos or formaldehyde free	GB656-2001
Water permeability	No moisture or water	CECS9597
Alkali Resistance		CECS9597
Thermal conductivity	0.109	Average temperature: 30±5 Kcal/m°chr