316L/304 Stainless Steel Welded Tube
Grade: 316L/304
Size: OD(6.35-1016MM), WT(0.5-8MM).
Standards: ASTM, JIS, DIN, EN, ISO, GB, GOST etc.
Finish: BA/AP/Polished/MF
Application: Boiler, heat exchanger, construction, hygiene, pharmacy, power, petrochemical, machinery and automobile industry
Package: Plywood case or bundles
ASTM A249/A269/A554/A270 TUBE, etc.
DIN11850/SMS/ISO2037/ISO1127 TUBE, etc.
JIS G3459/JIS G3448 PIPE, ASTM A312 PIPE, etc
GB/T12770/T12771 tube/pipe, etc.
316L/304 Stainless Steel Welded Tube
Material | ASTM A249 Chemical Composition % Max |
C | Mn | P | S | Si | Cr | Ni | Mo | N B | Nb | Ti |
TP304 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 18.0-20.0 | 8.0-11.0 | ^ | ^ | ^ . | ^ |
TP304L | 0.035 | 2.00 | 0.045 | 0.030 | 1.00 | 18.0-20.0 | 8.0-12.0 | ^ | ^ | ^ | ^ |
TP316 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | ^ | ^ | ^ |
TP316L | 0.035 D | 2.00 | 0.045 | 0.030 | 1.00 | 16.0-18.0 | 10.0-15.0 | 2.00-3.00 | ^ | ^ | ^ |
TP321 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | ^ | ^ | ^ | 5C -0.70 |
TP347 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 |
|
| 10C -1.10 | ^ |
Material | Heat treatment | Temperure F (C) Min. | Hardness |
Brinell | Rockwell |
TP304 | Solution | 1900 (1040) | 192HBW/200HV | 90HRB |
TP304L | Solution | 1900 (1040) | 192HBW/200HV | 90HRB |
TP316 | Solution | 1900(1040) | 192HBW/200HV | 90HRB |
TP316L | Solution | 1900(1040) | 192HBW/200HV | 90HRB |
TP321 | Solution | 1900(1040) F | 192HBW/200HV | 90HRB |
TP347 | Solution | 1900(1040) | 192HBW/200HV | 90HRB |
OD, inch | OD Tolerance inch(mm) | WT Tolerance % | Length Tolernace inch(mm) |
+ | - |
≤ 1 / 2 | ± 0.005 ( 0.13 ) | ± 15 | 1 / 8 ( 3.2 ) | 0 |
> 1 / 2 ~1 1 / 2 | ± 0.005(0.13) | ± 10 | 1 / 8 (3.2) | 0 |
> 1 1 / 2 ~< 3 1 / 2 | ± 0.010(0.25) | ± 10 | 3 / 16 (4.8) | 0 |
> 3 1 / 2 ~< 5 1 / 2 | ± 0.015(0.38) | ± 10 | 3 / 16 (4.8) | 0 |
> 5 1 / 2 ~< 8 | ± 0.030(0.76) | ± 10 | 3 / 16 (4.8) | 0 |
8~< 12 | ± 0.040(1.01) | ± 10 | 3 / 16 (4.8) | 0 |
12~< 14 | ± 0.050(1.26) | ± 10 | 3 / 16 (4.8) | 0 |