Construction Waterproof Coatings as Waterproof Layer in Interior Rooms

Product Specifications

Prod Model:	FB-0001
Markets:	Southeast Asia,Africa,Oceania,Mid East,Western Europe
Solid Content:	94%
Appearance:	Black Liquid
Thinkness:	1.5-2.0mm
Applied Area:	Bathroom,Kitchen,Pool,Roof
Applied Ways:	Brush or Spray
Package:	Metal Bucket
Tensile Strength:	2.19MPa
Elongation At Break:	>700
Initial Setting Time:	4h
Finial Setting Time:	8h
Type:	Roofing and Waterproofing
Ceiling Tile Shape:	Liquid
Material:	PU
Thickness:	1.5mm
Ceiling Tile Type:	Mineral Wool Ceilings
Surface Treatment:	Film Coated
Function:	Waterproof
Certification:	MSDS
Color:	Black
Usage:	Kitchen,Bathroom,Roofs,Balcony,Pools;

Product Description

Introduction:
      One-component Polyurethane Waterproof Coating is a kind of high grade waterproof coating,I
socyanate and polyether polyol as main raw material,mixed with accessory ingredients and resin.
 
Characteristics:
   1 Single component, convenient to use . High cohesive force and ductility.
   2 Resistance to chemical corrosion,resistance to low temperature, anti-aging,does not get moldy
   3 Without any solvent.Terminal group NCO in the coating solid and conjunctiva after contact with air. 
This product is environmental and healthy.
 
 Methods: 
        Stir the paint with a brush or roller brown uniform rolling brush. Brushing base surface dry and no surface dust.
 Ambient temperature of 23 C,8h in the conjunctiva, the low temperature longer, whereas shorter.
 After curing the first pass,and then cover the second time scraping. Scraping direction must be perpendicular to
 the first pass. If the thickness of the coating reach the design,to achieve the required thickness of brushing up.
 Announcements:
     The coating must be fully cured before impoundment,rain and fog can not do outdoor construction. Paint solvents,can not add special solvent.Product storage and transportation in the anti-sun and rain, within the temperature 5C-40C. Stored in the shade. The company's only product quality 
problems responsible for the exchange of materials. Pls use it after inspection. 

	Item		Data
1	Appearance		Well-proportioned  heavy body ,without gel
2	Tensile Strength,MPa		2.19
3	Elongation at break,%		762
4	Tearing Strength,Mpa		19
6	Watertightness (0.3MPa, 30min)		watertight
7	Solid Content ,%		94
8	Surface drying time (h)		4
9	Hard drying time (h)		8
10	Heating ratio of expansion and contraction		--1.7C
12	Aging Situation	Heat aging	No crack or deformation
		Artificial weathering aging	No crack or deformation
13	Heating Treatment	Retention Tensile Strength%	147
		Elongation at break,%	876
		Foldability at Low Temperature(-35C)	No crack or deformation
14	Alkali Treatment	Retention Tensile Strength%	106
		Elongation at break,%	880
		Foldability at Low Temperature(-35C)	No crack or deformation
15	Acid Treatment	Retention Tensile Strength%	102
		Elongation at break,%	806
		Foldability at Low Temperature(-35C)	No crack or deformation
16	Artificial weathering aging	Retention Tensile Strength%	143
		Elongation at break,%	803
		Foldability at Low Temperature(-35C)	No crack or deformation