Heating Resistant Wire Alloy 145 Resistance Wire

Name: Heating Resistant Wire Alloy 145 Resistance Wire
Brand: China-Manufacturer-Directory.com
SKU: 766150615
Availability: InStock
Rating: 4.9 (128 reviews)

Supplier:	Hangzhou Ualloy Material Co., Ltd.
Price:	US $ 6.5kg
Min Order:	30Kg
Quantity::
Trade Terms:	FOB,CFR,CIF

Product Specifications

Prod Model:	Resistohm 145
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Status:	Bright
Density:	7.1
Tensile Strength:	637-784
Melting Point:	1500
Product Type:	Wire
Carbon Content:	Low Carbon
Material:	Fecral

Product Description

Alloy 875
22% Chrome, 72.2% Iron, 5.8% Aluminum
875 ohms/cmf 1500C melt point.
Also called Kanthal A1, Kanthal, Alloy 875, Resistohm 145, Aluchrom 0, Alchrome 875, MWS-875, Stablohm 875

FeCrAl wire, Iron Chrome Aluminum wire is very popular in industrial heating heaters and furnaces. We supply them as the requirements, such as temperature and resisitivity.

Conventional Product specifications: 0.5 ~ 10 mm

Packaging: Wooden case. Inside package, carton, wooden pallet

Advantages
1. High atmosphere temperature
2. Long life
3. High surface load
4. Good oxidation resistance
5. Small proportion
6. High resistivity
7. Good sulfur resistance

Properties\Grade		1Cr13Al4	0Cr21Al4	0Cr21Al6	0Cr23Al5	0Cr25Al5	0Cr21Al6Nb	0Cr27Al7Mo2
Main Chemical Composition(%)	Cr	12.0 ~ 15.0	18.0 ~ 21.0	19.0 ~ 22.0	22.5 ~ 24.5	23.0 ~ 26.0	21.0 ~ 23.0	26.5 ~ 27.8
	Al	4.0 ~ 6.0	3.0 ~ 4.2	5.0 ~ 7.0	4.2 ~ 5.0	4.5 ~ 6.5	5.0 ~ 7.0	6.0 ~ 7.0
	Fe	Balance	Balance	Balance	Balance	Balance	Balance	Balance
	Re	Opportune	Opportune	Opportune	Opportune	Opportune	Opportune	Opportune
							Nb:0.5	Mo:1.8-2.2

Mechanical Properties
Grade	0Cr21Al6	0Cr25Al5	0Cr23Al5	1Cr13Al4	0Cr21Al6Nb	0Cr21Al4	0Cr27Al7Mo2
Max Continuous Service Temp	1250 ºC	1250 ºC	1250 ºC	950 ºC	1350 ºC	1100 ºC	1400 ºC
Resisivity at 20ºC	1.42 ±0.07 ohm mm2/m	1.42 ±0.06 ohm mm2/m	1.35 ±0.07 ohm mm2/m	1.25 ±0.08 ohm mm2/m	1.45 ±0.07 ohm mm2/m	1.23 ±0.06 ohm mm2/m	1.53 ±0.07 ohm mm2/m
Density	7.16 g/cm3	7.10 g/cm3	7.25 g/cm3	7.4 g/cm3	7.10 g/cm3	7.35 g/cm3	7.1 g/cm3
Thermal Conductivity	63.2 KJ/m@h@ ºC	46.1KJ/m@h@ ºC	60.2KJ/m@h@ ºC	52.7 KJ/m@h@ ºC	46.1 KJ/m@h@ ºC	46.9 KJ/m@h@ ºC	45.2 KJ/m@h@ ºC
Coefficient of Thermal Expansion	14.7×10-6/ ºC	16.0×10-6/ ºC	15.0×10-6/ ºC	15.4×10-6/ ºC	16.0×10-6/ ºC	13.5×10-6/ ºC	16.0×10-6/ ºC
Melting Point	1500 ºC	1500 ºC	1500 ºC	1450 ºC	1510ºC	1500 ºC	1520 ºC
Tensile Strength	637~784 Mpa	637~784 Mpa	637~784 Mpa	588~735 Mpa	637~784 Mpa	637~784 Mpa	637~784 Mpa
Elongation	Min 12%	Min 12%	Min 12%	Min 12%	Min 12%	Min 12%	Min 10%
Section Variation Shrink Rate	65~75%	65~75%	65~75%	65~75%	65~75%	65~75%	65~75%
Repeatedly Bend Frequency	Min 5 times	Min 5 times	Min 5 times	Min 5 times	Min 5 times	Min 5 times	Min 5 times
Hardness	200-260HB	200-260HB	200-260HB	200-260HB	200-260HB	200-260HB	200-260HB
Micrographic Structure	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic Property	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic

Hangzhou Ualloy Material Co., Ltd is a high-tech enterprise which specialized in making all kinds of alloy strip such as high resistance alloy, low-resistance copper nickel alloy, precision alloy, FeCrAl alloy for exhaust purifier.

HangZhou Ualloy Material Co., Ltd have a full production line from melting, surface cleaning, rolling and slitting, full set of testing machine and can meet all kinds of technical requirement from customer. Our product is widely used in heating equipment, big steel mill, mineral, electrical equipment, food machinery, auto industry, aerospace industry. Our product not only is popular in domestic market, but also been exported to all over the world.

Our company aims to be the best-quality alloy strip producer in the world. We insist on developing the more advanced alloy strip technology, to serve all the customer, improve people's living level, make a more green earth in the future.