Intrduction:
Pvc waterproof membrane
Is an excellent high-quality polymer waterproof sheet, made of PVC resin by adding plasticizer, anti-UV agent, anti-aging agent, and stabilizer and other processing aids through extrusion and molding. As the highly-recommended product by the Ministry of Construction, it is featured by high tensile strength, great elongation, good stability, small shrinkage, low-temperature performances, good resistance to weathering and root penetration, and long service life
Specification:
1>Thickness: 1.20mm, 1.50mm, 1.80mm, 2.00mm.
2>Length: 15M, 20M, 25M.
3>Width: 1.00M, 2.00M, 2.05M.
4>Color: White, grey, green, black etc.
5>All the specifications can be customized.
Application:
Due to unique product formulation,
The product has the longer life far beyond the usual waterproof material.
The entire water system is over 30 years on the roof and 50 years underground.
It is widely used in construction and civil engineering. It has high tensile strength,
Great elongation, and small size change during heat treatment.
Loading:
20ft container: 1> 1.5mm thickness can loading 10496 m2, 2.1kg/m2
2> 2.0mm thickness can loading 7687.5m2, 2.7kg/m2
Features:
1. Good combination of high elasticity and tensile strength.
2. Fine resistance to static electricity.
3. Excellent resistance to ageing / weathering.
4. Durable, the effective age can be more than 20 years used on exposed surfaces, used on non-exposed surfaces, it can reach 50 years.
5. Fine flexibility at low temperature, adaptable to cold conditions.
6. Root-resistance, can be used on the planting roofs.
7. Fine puncture resistance, joint peel strength and joint shear strength.
8. Fine UV-resistance, no pollution to environment.
9. Easily welding, installing, secure.
10. Easy treatments to the delicate parts of corners and edges.
11. Convenient maintenance with low cost.
Application method
PVC waterproof membrane can variously be used to the roof of building,
Underground building, tunnel, dam, pool, sewage treatment works,
Garbage disposal facilities. It also can be suitable to any requirement of
All kinds of technological practice & different grade of roof waterproof and
Underground constructions waterproof.
Model NO |
UWT-PVC |
Material |
PVC |
Thickness |
1.2mm, 1.3mm, 1.5mm, 2.0mm |
Width |
2.05m |
Color |
White, Green, Black, etc |
Export Markets |
Global |
Trademark |
UWT |
Standard |
ISO, SGS |
Production Capacity |
3000000sqms |
Packing |
Wrapped with Woven Bag |
Origin |
Shouguang, Shandong |
|
|
|
|
|
|
|
|
|
|
No. |
Project |
Index |
|
|
VH |
VL |
VP |
VG |
VGL |
1 |
The resin thickness of middle base/ mm ≥ |
__ |
0.40 |
2 |
Pull N/cm ≥ |
__ |
120 |
250 |
__ |
120 |
3 |
Elongation at break % ≥ |
200 |
150 |
__ |
200 |
100 |
4. |
tensile strength /MPA ≥ |
10.0 |
__ |
__ |
10.0 |
__ |
5. |
Elongation at maximum force / % ≥ |
__ |
__ |
15 |
__ |
__ |
6. |
Thermal dimensional change % ≤ |
2.0 |
1.0 |
0.5 |
0.1 |
0.1 |
7. |
Cold bending |
-25 celsius cracks |
8. |
watertightness |
0.3MPA, 2h impervious |
9. |
Shock resistance |
0.kg@m,watertight |
10. |
Anti static load a |
__ |
__ |
20kg watertight |
11. |
Peel strength seams /(N/mm) ≥ |
4.0 Or membrane damage |
3.0 |
12. |
right angle tear strength /(N/mm) ≥ |
50 |
__ |
__ |
50 |
__ |
13. |
Trapezoidal Tear Strength /(N/mm) ≥ |
__ |
150 |
250 |
__ |
220 |
14. |
water absorption (70 celsius ,168 h ) /% |
Soaking ≤ |
4.0 |
|
|
After to dry ≥ |
-0.40 |
15. |
Thermal aging treatment |
Exterior |
Bond cracks and holes no blistering |
|
|
Tensile Strength % ≥ |
85 |
__ |
__ |
85 |
__ |
|
|
Breaking elongation rate
% ≥ |
80 |
80 |
__ |
80 |
80 |
|
|
Time / h |
672 |
|
|
Maximum tension retention% ≥ |
__ |
85 |
85 |
__ |
85 |
|
|
Maximum tensile elongation rate % ≥
|
__ |
__ |
80 |
__ |
__ |
|
|
Cold bending |
-20 celsius no crack |
16. |
chemical resistance |
Exterior |
Bond cracks and holes no blistering |
|
|
Tensile Strength % ≥ |
85 |
__ |
__ |
85 |
__ |
|
|
Breaking elongation rate
% ≥ |
80 |
80 |
__ |
80 |
80 |
|
|
Maximum tension retention% ≥ |
__ |
85 |
85 |
__ |
85 |
|
|
Maximum tensile elongation rate % ≥
|
__ |
__ |
80 |
__ |
__ |
|
|
Cold bending |
-20 celsius no crack |
17. |
Artificial Weathering c |
Exterior |
Bond cracks and holes no blistering |
|
|
Tensile Strength % ≥ |
85 |
__ |
__ |
85 |
__ |
|
|
Breaking elongation rate
% ≥ |
80 |
80 |
__ |
80 |
80 |
|
|
Time / h |
1500 b |
|
|
Maximum tension retention% ≥ |
__ |
85 |
85 |
__ |
85 |
|
|
Maximum tensile elongation rate % ≥
|
__ |
__ |
80 |
__ |
__ |
|
|
Cold bending |
-20 celsius no crack |
Note:
a Anti static load only for roofing coiled material requirements.
b single-layer coil roofing products Artificial Weathering time is 2500 h
C Non exposed roofing membrane does not require the measurement Artificial Weathering
|
|
|
|
|
|
|
|
|
|
|
|
|