LLDPE Virgin/Plastic Raw Material/Plastic Granular

Product Specifications

Prod Model:	LLDPE
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Place Of Origin:	Hebi China
Quanlity:	Virgin
Service:	OEM/ODM
Usage:	Specialty Plastics
Material:	Linear Low Density Polyethylene/LLDPE
Color:	White

Product Description

1, LLDPE film grade

Tests	Value	Unit
Melt Flow Rate (MFR)	2.0±0.4	g/10min
Density	920±2	Kg/cm3
Tensile Strengthat Yield	8	Mpa ≥
Tensile Strengthat Break	12	Mpa ≥
haze	15	%≤
Packing	In 25 kg PP woven bags,20MT/20'FCL

2, LLDPE for Master Batch Use

Tests	Value	Unit
Melt Flow Rate (MFR)	20	g/10min
Density	0.924	g/cm3
Tensile Strength	MD12	Mpa
	TD 10
Elongation at Yield	13	%
Elongation at Break	200
Dark Drop Impact	105	g
Brittle Temperature(F 50)	-70	°C
Vicat Softening Point	90	°C
Packing	In 25 kg PP woven bags,20MT/20'FCL

3, LLDPE Powder Rotational Molding Grade for Tank Use

Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C

Tests Value Unit
Melt Flow Rate (MFR) 2.0± 0.4 g/10min
Density 920± 2 Kg/cm3
Tensile Strengthat Yield 8 Mpa ≥
Tensile Strengthat Break 12 Mpa ≥
Haze 15 %≤
Packing In 25 kg PP woven bags, 20MT/20'FCL

2, LLDPE Powder Rotational Molding Grade for Tank Use
Tests Value Unit
Melt Flow Rate (MFR) 3.2 g/10min
Density 0.939 g/cm3
Melting Point 127 ° C
Tensile Yield Strengt 21 Mpa
Tensile Strength at Break 28 Mpa
Elongation at Brea 1, 100 %
Flexural Modulus 750 Mpa
Brittle Temperature <-60 ° C

Application
1 Fiber (Carpet, Textiles, Upholstery, etc. )
2 Film (Shopping bags, casting film, multilayer film, etc. )
3 Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
4 Extrusion Molding (Sheet, Pipe, Wire & Cable, etc. )
5 Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc. )...