Product Specifications
| Prod Model: |
301#, 3#-4A, 4#-1E, 3#-5B, 3#-5C, 3#-5D |
| Markets: |
North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe |
| Shape: |
Block |
| Model: |
301#, 3#-4A, 4#-1e, 3#-5b, 3#-5c, 3#-5D |
| Application 1: |
Kraft Paper Sealing Tape |
| Application 2: |
Double Sides Adhesive Tape |
| Application 3: |
Foam Adhesive Tape |
| Application 4: |
Aluminum Foil Tape |
| Bonding Function: |
Structural Adhesive |
| Morphology: |
Solid-State |
| Classification: |
Hot Melt |
| Main Agent Composition: |
Rubber |
| Characteristic: |
Weatherability |
| Promoter Composition: |
Curing Agent |
| Composition: |
Inorganic Material |
| Color: |
Clear |
| Application: |
Tape |
| Material: |
Rubber |
Product Description
Pressure sensitive hot melt adhesive for tape
Application:
Pressure sensitve hot melt adhesive for kraft paper sealing tape: 301#
Pressure sensitive hot melt adhesive for double sides adhesive tape: 3#-4A
Pressure sensitive hot melt adhesive for foam adhesive tape, aluminium foil tape, PE film for batten: 4#-1E
Pressure sensitive hot melt adhesives for cloth tape: 3#-5B, 3#-5C, 3#-5D
Pressure sensitive hot melt adhesive for medical bandage and woundplast: AIGA Med. 1#
| Model | 3#-5B | 3#-5C | 3#-5D |
| Appearance | white opaque | white opaque | compositon:TPR |
| Solid content | 100% | 100% | 100% |
| Softening point | 85±5°C | 105±5°C | 80±5°C |
| Melting viscosity | 10000±2000mPa.s(160°C) | 20000±3000mPa.s(160°C) | 8000±1500mPa.s(160°C) |
| Initial bonding strength | ≥12# steel ball (tested at 23°C, coating weight 35 g/ m 2 ) | 11# steel ball (tested at 23°C, coating weight 100 g/ m 2 ) | ≥14# steel ball (tested at 23°C, coating weight 35 g/ m 2 ) |
| Permanent viscous | ≥48h | ≥48h | ≥48h |
| 180°peel strength | 18N/2.5cm | 18N/2.5cm | 14N/2.5cm |
| Oil penetration | 48 hours no penetration at 60°C constant temperature | 48 hours no penetration at 60°C constant temperature | 24 hours no penetration at 60°C constant temperature |
| Operation temperature | 150-180°C | 150-180°C | 150-180°C |
| Application | good bonding effect for fabric, paper and wood substrate. | cloth tape | good adhesion to cloth,paper and wood substrate |
| Model | 301# | 3#-4A | 4#-1E |
| Appearance | yellow transparent | pale yellow transparent | yellow transparent |
| Solid content | 100% | 100% | 100% |
| Softening point | 75±5°C | 83±5°C | 105±5°C |
| Melting viscosity | 5500±1000mPa.s(160°C) | 5000±1000mPa.s(160°C) | 3500±800mPa.s(160°C) |
| Initial bonding strength | 8# steel ball (tested at 23°C, coating weight 35 g/ m 2 ) | 8# steel ball (tested at 23°C, coating weight 35 g/ m 2 ) |
|
| Permanent viscous | ≥24h | ≥48h |
|
| 180°peel strength | 16N/2.5cm |
| ≥25N/2.5cm |
| Oil penetration | 48 hours no penetration at 60°C constant temperature | 48 hours no penetration at 60°C constant temperature | 48 hours no penetration at 60°C constant temperature |
| Operation temperature | 150-180°C | 150-180°C | 150-180°C |
| Application | kraft paper sealing tape | double sides tape | foam tape,aluminium foil tape,PE film for batten |
Wuxi Chiyang International Trading Co., Ltd. is a branch company of Shandong Chiyang Group, located in the famous Tourist City-Wuxi, China.
We are an innovative Global Trade Service provider for those professional manufacturers in different industry. Our team has abundant of experience in import and export, integrating our partner factories' production capability, R&D, Quality Control, we complement each other's advantages to provide the best products and service to customers from all over the world.
Our goal is to build a bridge between your market demands and the qualified factory, making your purchase more economically and efficiently.