Price: | US $ 1200/Ton |
---|---|
Trade Terms: | FOB,CFR,CIF |
Min Order: | 1/Ton |
Pay Type: | L/C,T/T,Paypal,Money Gram,Western Union |
Prod Model: | LLDPE-ZDY |
---|---|
Markets: | North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe |
Model Number: | R50035e |
Type: | R50035e |
Appearance: | Granule or Powder |
Application: | Film, Packing, Sheet, Container |
Test: | SGS/CIQ |
Feature: | High Quality with Best Price |
Grade: | LLDPE Film/Injection Moldel |
Sample: | Can Free Supply for Test |
Shape: | Powder,Pallets,Scrap,Resin |
Style: | Virgin/Recycled |
Usage: | Specialty Plastics |
Material: | Linear Low Density Polyethylene/LLDPE |
performance tests | Test conditions | Test Method | Test Data | Unit/data | |
basic performance | density | ASTM D-1505 | 0.935 | g/cm3 | |
MFR | ASTM D-1238 | 5.0 | g/10min | ||
mechanical property | tensile breaking strength | ASTM D-638 | 11.5 | Mpa | |
tensile yield strength | ASTM D-638 | 18 | MPa | ||
1%secant modulus(Extended) | ASTM D-790 | 500 | MPa | ||
bending strength | ASTM D-790 | 19.3 | MPa | ||
elongation at break | ASTM D-638 | 700 | % | ||
flexural modulus | ASTM D-790 | 724 | Mpa | ||
hardness | ASTM D-2240 | 69 | |||
environmental stress crack resistance | 100%Igepal,F50 | ASTM D-1693A | >300 | Hrs | |
Thermal Properties | vicat softening point | ASTM D-1525 | 115 | ºC | |
brittle temperature | ASTM D-746 | <-75 | ºC |
Tests | Value | Unit |
Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
Density | 920±2 | Kg/cm3 |
Tensile Strengthat Yield | 8 | Mpa ≥ |
Tensile Strengthat Break | 12 | Mpa ≥ |
haze | 15 | %≤ |
Packing | In 25 kg PP woven bags,20MT/20'FCL |
Tests | Value | Unit |
Melt Flow Rate (MFR) | 20 | g/10min |
Density | 0.924 | g/cm3 |
Tensile Strength | MD12 | Mpa |
TD 10 | ||
Elongation at Yield | 13 | % |
Elongation at Break | 200 | |
Dark Drop Impact | 105 | g |
Brittle Temperature(F 50) | -70 | °C |
Vicat Softening Point | 90 | °C |
Packing | In 25 kg PP woven bags,20MT/20'FCL |