Submerged Arc Welding Welding Flux Lj-Sj601 Agglomerated Flux
LJ-SJ601 Welding Flux GB/T17854 F308 Soldering Flux F316L
Flux type: Silicon-Manganese
Basicity index: 1.80
Compositions of fluxes (%) | SiO2+TiO2 | CaO+MgO | MnO+Al2O3 | CaF2 | S | P |
| 5-10 | 6-10 | 30-40 | 40-50 | ≤0.06 | ≤0.08 |
Typical deposited metal mechanical property | Wire matched | Yield Stress σ s MPa | Tensile Strength σ b MPa | Elongation δ 5% | AKV(J) |
| H0Cr21Ni10 | -- | >520 | >=30 | -- | -- |
Remark:- Before welding, fluxes should be baked for two hours at 300-350ºC.
- Removal of rust, oil, dirt, water, impurities, etc in welding areas.
Packing: 25kg/bag, pallets are available.
Performance: Low harmful element, excellent welding technique, easy slag removal inside the groove, nearly no carbon will be added while welding stainless steel.
Applications: Stainless steel and heat-resistance steel.
Contact: Miss Helen Duan
Tel/Fax: 0086-532-85641729
Laiwu jincai welding materials Co., Ltd, head office located in the laiwu city, subsidiary located in the qingdao that be responsible for foreign trade.
Our plant's output will be 20, 000 tons annual, the main products including fused flux \sintered flux \welding wire and welding electrod. also It's approved by CCS\GL etc.