SBR-1712 Specification Values (SH/T 1626-2005) | ||||||
Item | Property | Test Method | ||||
Grade A | Grade B | Grade C | ||||
Volatile Matter, % ≤ | ≤0.60 | ≤0.80 | ≤1.00 | GB/T 6737-1997 Hot Roll Method | ||
Ash, % ≤ | 0.5 | GB/T 4498-1997 Method A | ||||
Organic acid % | 3.90-5.70 | GB/T 8657-2000 | ||||
Soap,% ≤ | 0.5 | |||||
Bound styrene, %(m/m) | 22.5-24.5 | GB/T 8658-1998 | ||||
Oil, % (m/m) | 25.3-29.3 | 24.3-30.3 | SH/T 1718-2002 | |||
Mooney viscosity 50, ML(1+4)100ºC | 44-54 | 43-55 | 42-56 | GB/T 1232.1-2000 | ||
Compound 50, ML(1+4)100ºC≤ | 70 | GB/T 1232.1-2000 ASTM IRB No.7 | ||||
300%Modulus (145ºC)/Mpa | 25 min | 9.8-13.8 | 9.3-14.3 | GB/T 8656-1998 Method A | ||
35 min | 12.1-16.1 | 11.6-16.6 | ASTM IRB No.7 | |||
50 min | 13.0-17.0 | 12.5-17.5 | GB/T 528-1998 I type cutter | |||
Tensile strength (145ºC,35min), Mpa ≥ | 19.4 | 18.4 | ||||
Elongation (145ºC,35min), % ≥ | 380 | 370 | ||||
Specification | SBR-1712 is polluting oil-filled styrene-butadiene rubber, with excellent adhesion, abrasion resistance and processability. Widely used in tires, conveyor belts, hoses and general black rubber. | |||||
SBR-1502 Specification Values (GB/T12824-2002) | ||||||
Item | Property | Test Method | ||||
Grade A | Grade B | Grade C | ||||
Volatile Matter, % ≤ | ≤0.60 | ≤0.75 | ≤0.90 | GB/T 6737-1997 Hot Roll Method | ||
Ash, % ≤ | 0.5 | GB/T 4498-1997 Method A | ||||
Organic acid % | 4.5-6.75 | GB/T 8657-2000 | ||||
Soap,% ≤ | 0.5 | |||||
Bound styrene, %(m/m) | 22.5-24.5 | GB/T 8658-1998 | ||||
Mooney viscosity 50, ML(1+4)100ºC | 44-55 | 44-56 | GB/T 1232.1-2000 | |||
Compound 50, ML(1+4)100ºC≤ | 93 | |||||
300%Modulus (145ºC)/Mpa | 25 min | M±2.0 | M±2.5 | GB/T 8656-1998 Method A | ||
35 min | 20.6±2.0 | 20.6±2.5 | ||||
50 min | 21.5±2.0 | 21.5±2.5 | ||||
Tensile strength (145ºC,35min), Mpa ≥ | 25.5 | 24.5 | ||||
Elongation (145ºC,35min), % ≥ | 340 | 330 | ||||
Note | 1, What is listed in the table is the use of ASTM IRB No.7 mix synthetic rubber vulcanization performance indicators; 2.M is a number that needs to be negotiated by both supplier and buyer. | |||||
Specification | SBR-1502 is non-polluting, non-oil-filled SBR, has good tensile strength, abrasion resistance and flex. Widely used in light-colored rubber products, such as transparent shoes, colored tires, blankets, medical products, etc., it can be applied to tires, conveyor belts, hoses and other ferrous products. | |||||
SBR-1500 Specification Values (GB/T8655-2006) | ||||||
Item | Property | Test Method | ||||
Grade A | Grade B | Grade C | ||||
Volatile Matter, % ≤ | ≤0.60 | ≤0.80 | ≤1.00 | GB/T 6737-1997 Hot Roll Method | ||
Ash, % ≤ | 0.5 | GB/T 4498-1997 Method A | ||||
Organic acid % | 5.00-7.25 | GB/T 8657-2000 Method A | ||||
Soap,% ≤ | 0.5 | |||||
Bound styrene, %(m/m) | 22.5-24.5 | GB/T 8658-1998 | ||||
Mooney viscosity 50, ML(1+4)100ºC | 44-57 | 46-58 | 45-59 | GB/T 1232.1-2000 | ||
Compound 50, ML(1+4)100ºC≤ | 88 | GB/T 1232.1-2000 use ASTM IRB No.7 | ||||
300%Modulus (145ºC)/Mpa | 25 min | 11.8-16.2 | 10.7-16.3 | - | GB/T 8656-1998 Method A use ASTM IRB No.7 | |
35 min | 15.5-19.5 | 14.4-20.0 | 14.2-20.2 | |||
50 min | 17.3-21.3 | 16.2-21.8 | - | |||
Tensile strength (145ºC,35min), Mpa ≥ | 24 | 23 | 23 | GB/T 528-1998 I type cutter | ||
Elongation (145ºC,35min), % ≥ | 400 | |||||
Specification | SBR-1500 is polluted non-oil-filled styrene-butadiene rubber, raw rubber adhesion and excellent processability, vulcanized rubber wear resistance, tensile strength, tear strength and good resistance to the old properties. Widely used in dark products such as tires, conveyor belts, hoses, rubber and other black rubber products. |
Markets: | North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe |
---|---|
Material: | Styrene Butadiene Rubber |
Appearance: | Granules |