Price: | US $ 4.8/Square Meter |
---|---|
Trade Terms: | FOB,CFR,CIF |
Min Order: | 2000/Square Meter |
Pay Type: | L/C,T/T |
Prod Model: | UWT-4-800 |
---|---|
Markets: | North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe |
Model No: | Uwt-4-800 |
Length: | 20m |
Width: | 1m 1.5m 2.05mm |
Ceiling Tile Shape: | Roll |
Function: | Waterproof |
Surface Treatment: | Roll Coated |
Certification: | CE |
Usage: | Outdoor |
Type: | Waterproof Roll Material |
Color: | White |
Thickness: | 1.2mm 1.5mm 1.8m 2.0mm |
Material: | Tpo |
Ceiling Tile Type: | Polyester Tire |
TPO Membrane | Standard: Q/0783WHY | ||||||||||||||
NO. | Item | Unit | Value | ||||||||||||
N | L | P | |||||||||||||
I | II | ||||||||||||||
1 | Resin Thickness on Middle Mesh ≥ | mm | 0.4 | 0.4 | |||||||||||
2 | Tensile Properties | Max. Strength ≥ | N/cm | - | 200 | 196 | 250 | ||||||||
Tensile Strength ≥ | Mpa | 12.0 | - | - | - | ||||||||||
Elongation at Max. Strength ≥ | - | - | 15 | 15 | |||||||||||
Breaking Elongation ≥ | % | 500 | 250 | - | - | ||||||||||
3 | Dimensional Stability after Heat Treatment ≤ | % | 2.0 | 1.0 | 1.0 | 0.5 | |||||||||
4 | Foldability at Low Temperature | -40º C No cracks | |||||||||||||
5 | Watertightness | 0.3Mpa, 2h No penetration | |||||||||||||
6 | Resistance to Impact | 0.5kg*m, No penetration | |||||||||||||
7 | Resistance to Static Loading | - | - | 20kgs No penetration | |||||||||||
8 | Joint Peel Strength | N/mm | 4.0 or membrane broken | 3.0 | |||||||||||
9 | Overlap Joint Strength ≥ | N | - | 290 | |||||||||||
10 | Right Angle Tearing Strength | N/mm | 60 | - | - | ||||||||||
11 | Joint Shear Resistance | N/mm | - | 245 | 245 | 450 | |||||||||
12 | Water Absorption (70º C, 168h) ≤ | % | 4.0 | 3.0 | |||||||||||
13 | Aging in Hot Weather (115º C) | Time | 672h | ||||||||||||
Appearance | No bubbles, cracks, layering, sticky, hole | ||||||||||||||
Max. Tensile Retention Rate ≥ | % | - | 90 | ||||||||||||
Tensile Strength Retention Rate ≥ | % | 90 | - | - | |||||||||||
Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 90 | |||||||||||
Breaking elongation Retention rate | % | 90 | 90 | - | |||||||||||
Low Temperature Flexibility | -40 No cracks | ||||||||||||||
14 | Mechanical Erosion Resistance | Appearance | No bubbles, cracks, layering, sticky, hole | ||||||||||||
Max. Tensile Retention Rate ≥ | % | - | 90 | 90 | |||||||||||
Tensile Strength Retention Rate ≥ | % | 90 | - | - | |||||||||||
Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 90 | |||||||||||
Breaking elongation Retention rate | % | 90 | 90 | - | |||||||||||
Low Temperature Flexibility | -40º C No cracks | ||||||||||||||
15 | Artificial aging | Time | 1500h | ||||||||||||
Appearance | No bubbles, cracks, layering, sticky, hole | ||||||||||||||
Max. Tensile Retention Rate ≥ | % | - | 90 | 90 | |||||||||||
Tensile Strength Retention Rate ≥ | % | 90 | - | - | |||||||||||
Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 90 | |||||||||||
Breaking elongation Retention rate | % | 90 | 90 | - | |||||||||||
Low Temperature Flexibility | -40 No cracks | ||||||||||||||
Remark: l Resistance to static load is for TPO membranes used on roofings l The time of artificial aging of single-ply roofing membrane is 2500h |