High property electronic Silicone adhesive for LED electronic
Features
1. SI 3225A/B is used in potting protection of varied components. It can vulcanize to deep layer. The two components have a good fluidity after mixing. You can adjust the proportion of curing agent while operating. It's primerless and bonding well with most materials. It can be used to fix the accessories and resist water, dust and leakage current.
2. Double component high clarity liquid silicone adhesive, condensation dealcoholization.
3. Low viscosity, easy to process and operate.
4. Low hardening condensation, no corrosion and unstressing.
5. Excellent insulativity and stability in high temperature.
6. Excellent bonding, good water-proof and moisture-proof.
Usage:
1. Electronic and modules of automobile.
2. Power control module.
3. LED display screen.
4. LED spotlight, LED wall washer, Broad Area Linear Lights and fluorescent lamp.
Operation:
1. Mixing uniformity in the packing before using.
2. Maxed A, B component as the weighing ratio of 10: 1, mixing, and injected to the protection components (or modules) which need potting directly. In order to reduce the bubbles, injected slowly along the walls of the implement...
3. Let the components sit, out of bubble by themselves, heat curing or curing in the room temperature after the bubble disappeared, need about 1-6hours.
4. About potting equipment please contact our Marketing Department
Note:
1. It can improve the performance of the hardened by vacuum defoaming for mixed component.
2. After use, please seal the package.
3. The curing speed will be slow in the low temperature, suggest workshop in constant temperature.
The temperature is too low will lead curing speed Pianman, the proposed workshop thermostat
4. Once SI3225 contact with sulfur, amine, tin material would be difficult to sclerosis.
Package
1. A component 10kg Barrel, B component 1kg Bottle
2. Other packing can be customized
Storage
B component should be keep in cool and ventilative place
Shelf life: 12 months (25° C)
Transport as non-dangerous Article.
|
Properties before curing |
|
Component |
3225T |
3225W |
3225B |
|
A |
B |
A |
B |
A |
B |
|
Appearance |
Transparent fluid |
Transparent fluid |
White black
Thick liquid |
Transparent
fluid |
Black fluid |
Transparent
fluid |
|
viscosity, mPa@s(25° C) |
1500 |
100 |
3500 |
100 |
2500 |
100 |
|
Density, g/cm3(25° C) |
1.02 |
0.98 |
1.12 |
0.98 |
1.12 |
0.98 |
|
Mixture/mass ratio |
A:B = 100:(10±3) |
|
Viscosityafter mixing(mPa@s(25° C) |
1,000 |
2,500 |
1700 |
|
Operation time after mixing, min(25° C) |
50 |
20_9 |
|
Curing condition, min,25° C |
240 |
50-300 |
|
Properties after curing |
|
Appearance |
Colorless transparent elastomer |
White elastomer |
Black elastomer |
|
Hardness, shore A |
21 |
25 |
21 |
|
Tensile strength, MPa |
1.2 |
1.5 |
1.5 |
|
Shear strength, MPa |
0.3 |
0.7 |
0.7 |
|
Dielectric strength, KV/mm |
≥20 |
|
Volume resistance DC500V, Ω@cm |
1.1×1014 |
|
Loss factor (1 MHz) |
<0.008 |
|
Dielectric constant (1 MHz) |
<3.00 |
|
Service temperature, ° C |
- 50 -200 |
Founded in DEC. 2003, SEPUNA has been engaged in researching, manufacturing and marketing automobile sealant and adhesive for 9 years.
Since the foundation, SEPUNA Chemical has been focusing on adhesive's researching and application. Then in 2005, We acquired PUNADE technology which is from Switzerland.
Within 9 years, SEPUNA mainly develops Silicone, Polyurethane and Epoxy resin adhesives. And in the future, we will enlarge our line to Unsaturated, Natural and Acrylic Resin adhesive.
After 9 years' improvement, by the keep researching and innovation, SEPUNA is already a mature adhesive supplier with the core competitiveness.