Shanghai Lontom Electric Material Co., Ltd. >> Electric Insulating Edge Banding Tape

Electric Insulating Edge Banding Tape

Name: Electric Insulating Edge Banding Tape
Brand: China-Manufacturer-Directory.com
SKU: 643516555
Availability: InStock
Rating: 4.5 (83 reviews)

Supplier:	Shanghai Lontom Electric Material Co., Ltd.
Price:	Negotiable/Roll
Min Order:	1000/Roll
Quantity::
Trade Terms:	FOB,CFR,CIF

Product Specifications

Prod Model:	LT-PGW
Markets:	North America,South America,Eastern Europe,Southeast Asia,Mid East,Western Europe
Thickness:	0.17mm,0.2mm,0.25mm,0.3mm,0.32mm
Width:	10mm,15mm,20mm,25mm,30mm,32mm,35mm,40mm
Raw Material:	Fiber Glass Yarn + Unsaturated Polyester Rein
Package:	50~200 Meters Per Roll
Thermal Grade:	F, H Grade
Application:	Motor
Type:	Solid
Chemistry:	Inorganic Insulation
Thermal Rating:	H 180
Maximum Voltage:	20KV~100KV
Material:	Glass Fiber

Product Description

Electric Insulating Edge Banding Tape
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS

The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.

It's widely used in AC. DC motors, generators and transformers especially in traction motors.

Main Properties:

1.Thickness: 0.20mm±10%,0.30mm±10%

2.Width: 10mm~50mm±10%

3.Length/Spool: 50~200 meters

4.Standard color: White

5.Thermal Grade: F grade(155ºC)
H grade(180ºC)

6.Curing condition (Time to bring the piece to the temperature is not considered)

Temperature	ºC	160	150	135	120	115
Time	hour	2.5	3	5	14	20

7.Storage Stability:

Storage temperature	ºC	10	15	20	30
Time	Month	20	15	10	6

Technical Data:

Test content	Unit	Standard Value
Thermal class		H	F
Volatile content	%	≤ 2
Loss of weight at calcination	%	26±2
Soluble resin content	%	≥ 90
Tensile strength before curing	N/cm	≥1500	≥1000
Maximum pull while banding	N/cm	800	800
Tensile strength of ringlike sample at room temperature after curing	Mpa	20ºC
	Mpa	above :900	above :900
Tensile strength of ringlike sample at working temperature after curing	Mpa	180ºC	150ºC
	Mpa	≥600	≥560
Proof tracking index		≥500V
Arc resistance	S	≥160
Breakdown voltage parallel to layers	KV	normal condition:≥25 after soaked in water for 24 hours:≥10
Thermosetting	OK
Loss of tensile strength after soaked in oil	≤10%
Loss of tensile strength after soaked in oil	≤10%

Package:

Lontom Products manufactures and distributes the largest selection of heat shrink tubing, Electric Insulation Sleeving, Tape and wires split loom products, and sold insulation material and wiring accessories throughout the world.Lontom has delivered excellence by consistently providing our customers with extraordinary levels of quality, competitive pricing, service and timely deliveries.We believe providing personalized and professional customer service is essential.Additionally, by manufacturing our own products and partnering with qualified suppliers, we guarantee that our products and services will meet or exceed each of our customer's specific needs.

Exceptional service combined with a large selection of products for varying applications and industries have been the key to Lontom's success over the past seven years.Our staff of professionals truly cares about their respective customer responsibilities;They take the time to listen and respond accordingly.