Product Description
High Strength Extrusion Composites Epoxy Resin ZEF-022
1. Introduction:
High Strength Extrusion Composites Epoxy Resin is composed of low viscosity, toughness epoxy resin, modified anhydride hardener and accelerators. It offers low viscosity, long pot life, high temperature curing speed and good extrusion technology. Cured product has good erosive endurance, insulation and high comprehensive performance properties. The resin is used for carbon fiber, lass fiber extrusion products, such as all kinds of insulator FRP rod materials, casing pipe, building structures, etc.
2. Operating Process:
1. Take A Part and B Part according to ratio, and matched inner mold release agent(A part 1-2%) into a electric mixer, then fully mixing 5-10mins; We suggest that use tooth disc spreader, and try to reduce air bubbles.
2. Mixed adhesive pour into dip tank (tank temp 20-40 oC). Tidying up and drying of fiber, match with rata, and begin to dipping, extrusion and after curing.
3. Notice:
Since curing agent is easy to absorb moisture, Close the cans after the usage, avoid the long exposure. Caution against moisture.
Little quantity for each equipped adhesive, but must ensure that accurate measurement of consistency, and run out it in a short time. If squeeze out excess adhesive in extrusion process, should be even back to resin dip tank immediately, and supplement new adhesive to ensure the adhesive has good uniformity. To clean up adhesive dip tank if stop time is longer. Since over the period of use, adhesive viscosity is high even gel, which affect the infiltration effect of resin and fiber.
Model No.
Property |
ZEF-022
ZEF-022A ZEF-022B |
|
|
Viscosity mpa.s 25 o C |
3000-6000 50-150 |
|
|
Density g/cm 3 |
1.12-1.14 1.20-1.22 |
|
|
Mixing Ratio(weight) |
100 : 100-105 |
|
|
Viscosity after mixed 25 o C MPA.S |
300-500 |
|
|
160o CGel time S 180o C |
45-50
20-25 |
|
|
Pot life |
25o C 8-10hours |
|
|
Reference extrusion condition |
MoldIarea 130-140o C ,IIarea 140-150o C ,IIIarea 150-160o C ,post-cure 180-200o C ,
extrusion speed0.3-0.5m/min,can be adaptive to extrusion size. Mold Length 0.8-1.2m. |
Cured Neat Resin Properties :
|
property |
ZEF-022 |
|
Flexural Strength MPa |
110-120 |
|
Flexural Modulus MPa |
2800-3000 |
|
Tensile Strength MPa |
60-70 |
|
Tensile Modulus MPa |
2000-2200 |
|
Elongation at break% |
4-6 |
|
Impact strength kJ/m 2 |
20-25 |
|
Glass-transition temperature Tgo C |
100-110 |
Hubei Gemvon Chemicals Co., Ltd. Locates in state-leveled Wuhan, HuBei province. It has an area of 14, 000 m2 and mainly engages in developing, producing and selling epoxy resin(high temperature resistant CAS: 28768-32-3). We have the advanced plants, production capacity is over 1000tons per year. We attach great importance to Product Quality, Management and Enterprise Management, our plant has been gotten with ISO9001: 2000 Quality Management System Certification and ISO14001: 2004 Environment Management System Certification. Our plants have advanced technology, comprehensive analysis devices, strong technical support and research capabilities. Always welcome domestic and oversea customers come to talk about business cooperation!