Shanghai Sepuna Chemical Technology Co., Ltd. >> Two Component High Strength Epoxy Adhesive (SE2225)

Two Component High Strength Epoxy Adhesive (SE2225)

Name: Two Component High Strength Epoxy Adhesive (SE2225)
Brand: china-manufacturer-directory.com
SKU: 741241305
Availability: InStock
Rating: 4.7 (92 reviews)

Supplier:	Shanghai Sepuna Chemical Technology Co., Ltd.
Price:	US $ 2.26-3.58KG
Min Order:	1000KG
Quantity::
Trade Terms:	FOB,CFR,CIF

Product Specifications

Prod Model:	SE2225
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia
Brand Name:	Punade
OEM:	Acceptable
Package:	2310ml Tube, 210kg/Bottle
Shelf Life:	12 Months
MOQ:	500~2000 Kgs
Samples:	Free Samples
Certificate:	CE, SGS, ISO9001:2000, MSDS, Rosh, Reach
Place Of Origin:	Shanghai, China
Delivery Time:	Sample Order:2-3 Days; MOQ Order:7-10 Days
Classification:	Room Curing
Application:	Electronic Products/ Component
Material:	Epoxy
Morphology:	Viscous Body
Color:	Beige
Characteristic:	Cracking, Moisture, Pollution Resistance

Product Description

Two Component High Strength Epoxy Adhesive (SE2225) SE2225 is two component adhesive, it can cure in room temperature or by heating. After mixing part A and part B by 1:1, the adhesive cures in short time and be protection. Features 1. Resistance of moisture, pollution and other atmospheric constituent 2. High tensile, excellent adhesive property, cracking resistance and ductibility 3. ？Good anti-pollution, the require of surface pretreatment is low 4.？ Solvent free, no by-product in curing 5.？ Good temperature resistance, -50ºC~150ºC 6.？ Good bonding with glass fabric and steel metal Use Use for bonding metal, SMC FRP, aluminum honeycomb pane and electrical machine shank and Nomex paper. It's proper for VPI craft, glass fiber bonding, automobile parts assembling etc. Operation 1. Mix Part A and Part B by 1:1 evenly, seal the parts after using. 2. Stirring by one direction for avoiding the bubbles; the frame and bottom also need to be stirred evenly, or it will cause not cure situation. 3. Low temperature will slow the curing speed, if the primary strength can't get, the application environment needs to do constant temperature control. 4. Taking care of the material mouth seal in using Package？？？？？？？？？？？？？？？？？？？？？？？？？？？？？？？？？？ Storage 2*310ml Tube, 2*10kg/bottle ？？|||||||||||| ？？？？？？？？？？？Seal and Avoid light and light Or？ 2*20kg/drum ？？？？||||||||||||| ？？？？？？？？？？？？？ Temperature≤25ºC, humidity≤50%RH Shelf life: 6 months

Properties before curing
Part	A	B
Component	Beige viscous body	Beige viscous body
Viscosity, mPa.s(25 ºC )	75,000	56,000
Density, g/cm3(25 ºC )	1.35	1.35
Mixture/mass ratio, weight	A:B = 100:100
Mixture/mass ratio, volume	A:B = 100:100
Viscosity after mixing,mPa.s (25 ºC )	65,000
Density after mixing, g/cm 3 ,25 ºC	1.35
Operation time after mixing, min(25 ºC )	10
Preliminary curing time(min)	25 ºC 25 mins or 65 ºC 6 mins
Properties after curing
Hardness, Shore D	80
Shear strength, Mpa,Al/Al	17
Heat conductivity, W/mK	0.35
Expansion parameterμm/(m, ºC )	60
Water absorption 24h,25 ºC ,%	<0.3
Dielectric strength, KV/mm	>15
Loss factor(1 MHz)	0.014
Dielectric constant (1 MHz)	3.53
Volume resistance DC500V, Ω@cm	1.2×10 15

Founded in DEC. 2003, SEPUNA has been engaged in researching, manufacturing and marketing automobile sealant and adhesive for 9 years.

Since the foundation, SEPUNA Chemical has been focusing on adhesive's researching and application. Then in 2005, We acquired PUNADE technology which is from Switzerland.

Within 9 years, SEPUNA mainly develops Silicone, Polyurethane and Epoxy resin adhesives. And in the future, we will enlarge our line to Unsaturated, Natural and Acrylic Resin adhesive.

After 9 years' improvement, by the keep researching and innovation, SEPUNA is already a mature adhesive supplier with the core competitiveness.