Silicon-Mullite Brick

Product Specifications

Prod Model:	JD-106
Markets:	North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Al2O3:	63
Refractoriness:	1790
Bd (g/cm3):	2.6
CCS MPa:	110
Mor MPa:	15
0.2MPa Rul:	1650
Tsr(1100 Water-Cooling):	12
Cwt (Cc):	8.2
Refractoriness (',℃):	1580< Refractoriness< 1770
Feature:	Long Time Materials
Type:	Refractory Material
Shape:	Brick
Material:	Al2O3, Sic

Product Description

Silicon-mullite brick
 
Characters of Silicon-mullite brick:
 
Mullite (3Al2O3.2SiO2) and silicon carbide (SiC) are used as the main mineral composition of such burnt brick. It has advantages of resisting high temperature from mullite and wear-resisting corrosion resistance and good heat conduction performance from SiC. 
According to the previous user feedback, Silicon-mullite brick is of good thermal shock resistance, good high temperature strength, erosion resistance, not peeling off, don't break, longer service life. 
Applications of Silicon-mullite brick:
 
Silicon-mullite brick is mainly used for small and medium-sized the transition zone of cement kiln, decomposition furnace and cooling machine.  

Physical and Chemical Index.
 

Item and Index	Anti-stripping alumina brick	Silicon-mullite brick
	YRS-70	AZM-1650	AZM-1680
Al2O3	70	63	60
ZrO2	6-7	--	--
Refractoriness(ºC)	1790	1790	1790
BD (g/cm3)	2.5	2.6	2.5
AP(%)	23	20	20
CCS MPa	60	110	110
MOR MPa	12	15	16
0.2Mpa RUL(ºC)	1470	1650	1680
TSR(1100ºC water-cooling)	15	12	15
CWT (CC)	_	8.2	8.5
Note: the above two kinds of products are respectively used for cement rotary kiln decomposition zone, transition zone, wicket, High temperature wall of cooling machine, kiln mouth parts, etc.

 
Silicon-mullite brick packing
Bricks are packed on wooden pallet and then polyethylene film is placed over it, finally the package is tied up with steel strips.

Silicon-mullite brick MOQ
20 t as minimum quantity is accepted.

Silicon-mullite brick delivery time
30 days after receiving L/C or 30% of advanced T/T. the production capacity reach to 3000 t per month.